Usoro ọrụ na nkọwa nka nka nkeigwe nkedo ịkpụzi ájá
Nkwadebe ebu
Aluminom alloy dị elu ma ọ bụ ductile iron na-akpụ akpụ bụ nke a na-eme nke ọma site na sistemu CNC 5-axis, na-enweta ike dị elu n'okpuru Ra 1.6μm. Ụdị nkewa ahụ na-agụnye akụkụ akpụ (nke a na-emekarị 1-3º) na ohere igwe (0.5-2mm) iji kwado ịkwatu. Ngwa ụlọ ọrụ na-ejikarị akwa mkpuchi nwere akwa mgbagha dabere na zirconia iji gbatịa ndụ ọrụ gafere okirikiri 50,000.
Njuputa ájá & ịkpụzi
A na-agwakọta ájá silica nke nwere kemịkalụ (85-95% SiO₂) na ụrọ bentonite 3-5% na mmiri 2-3% maka ike akwụkwọ ndụ akwụkwọ ndụ kacha mma. Igwe na-akpụzi flaskless na-akpaghị aka na-etinye nrụgide compaction 0.7-1.2 MPa, na-enweta isi ike nke 85-95 na nha B. Maka ihe nkedo ngọngọ nke injin, a na-etinye sodium silicate-CO₂ cores siri ike nwere ọwa ikuku tupu emechi ebu.
Mgbakọ Akpụkpọ & Ndozi
Sistemụ ọhụụ robotic na-ahazi halves n'ime nnabata ± 0.2mm, ebe ntụtụ na-ejikọta ọnụ na-edobe ndebanye aha sistemu gating. C-clamps dị arọ na-arụ ọrụ ike 15-20kN, agbakwunyere site na ihe mgbochi ibu maka nnukwu ebu (> 500kg). Ụlọ ọrụ ntọala na-ejiwanye mkpọchi electromagnetic maka mmepụta dị elu.
Ịwụsa
Ọkụ na-etunye kọmpụta na-achịkwa na-edobe nnukwu ọkụ ọla na 50-80ºC karịa okpomọkụ mmiri. Sistemụ dị elu na-egosipụta sensọ ọkwa ọkwa laser yana ọnụ ụzọ mgbaba na-achịkwa PID, na-enweta nkwụsi ike ọnụego n'ime ± 2%. Maka aluminom alloys (A356-T6), ụdị ịgbasa ọsọ na-adịkarị 1-3 kg / sec iji belata ọgba aghara.
Njụjụ & Mgbakwunye
Oge nkwado na-esote iwu Chvorinov (t = k·(V/A)²), ebe k-ụkpụrụ dị iche site na 0.5 min/cm² maka akụkụ dị mkpa ruo 2.5 min/cm² maka nkedo dị arọ. Ntụnye atụmatụ nke exothermic risers (15-20% nke nkedo olu) na-akwụ ụgwọ maka mbelata na mpaghara dị oke egwu.
Shakeout & Nhicha
Ndị na-ebufe na-ama jijiji nwere ngwangwa 5-10G na-ekewa 90% nke aja maka iweghachi ọkụ. Nchacha ọtụtụ ọkwa gụnyere rotary tumblers maka nbibi mbụ, na-esochi ogbunigwe abrasive robot site na iji 0.3-0.6mm ígwè grit na 60-80 psi.
Nyocha & Post-Nhazi
Igwe ihe nchikota (CMM) na-enyocha akụkụ dị oke mkpa na ụkpụrụ ISO 8062 CT8-10. X-ray tomography na-achọpụta ntụpọ dị n'ime ruo na mkpebi 0.5mm. T6 ọgwụgwọ okpomọkụ maka aluminum gụnyere ngwọta na 540 ° C± 5 ° C na-esote ịka nká.
Isi uru:
Mgbanwe nke geometry na-eme ka arụ ọrụ oghere dị (dịka ọmụmaatụ, mgbapụta mgbapụta nwere ọkpụrụkpụ mgbidi 0.5mm)
Ihe dị iche iche na-agbasa alloys ferrous/abụghị ígwè (HT250 isi awọ ruo AZ91D magnesium)
40-60% obere ngwá ọrụ na-efu vs. ịnwụ nkedo maka prototypes
Mgbochi & Mbelata:
Mbelata ọrụ ike site na sistemu aja akpaaka
A na-edozi ihe mkpofu ebu site na 85-90% ọnụego mweghachi ájá
Oke imecha elu (Ra 12.5-25μm) meriri site na nhazi nkenke
Ụlọ ọrụ Quanzhou Juneng Machinery Co.,Ltd. bụ enyemaka nke Shengda Machinery Co., Ltd. ọkachamara na nkedo akụrụngwa.A elu-tech R&D Enterprise na ogologo oge na-arụ ọrụ na mmepe na mmepụta nke nkedo akụrụngwa, akpaka ịkpụzi igwe, na nkedo mgbakọ ahịrị.